Porous nanocomposite scaffolds prepared from gelatin and hydroxyapatite for bone tissue engineering: direct mixing and biomimetic
محل انتشار: نشریه نساجی و پلیمر، دوره: 11، شماره: 1
سال انتشار: 1402
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 71
فایل این مقاله در 14 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_ITAST-11-1_002
تاریخ نمایه سازی: 11 بهمن 1402
چکیده مقاله:
In this study, gelatin-hydroxyapatite (GEL/HA) composites as biological organic-inorganic composites were made up of the capability for use in hard tissue to be examined by two methods, direct mixing and biomimetic. In the direct mixing method, after the synthesis of hydroxyapatite, the resulting powder was mixed with gelatin; in the biomimetic method, hydroxyapatite was synthesized in the presence of gelatin. The thin layer composite substrates were prepared with a thickness of ۲ mm from the resulting mixture by combining methods including casting solvent and freeze-drying. The three-dimensional scaffolds were modified by glutaraldehyde as a crosslinked factor. The results showed that scaffolds have a high porosity of approximately ۸۸% and are interconnected with holes. According to the SEM image, the average pore size is around ۱۰۰ μm. A study of Infrared spectroscopy (FT-IR) and X-ray diffraction (XRD) indicated that the apatite phase formation non-stoichiometric low crystalline along with extensive replacement of carbonate ions on the network that is very biologically close to apatite phase and two composite components not only physically but also chemically interact with each other. Compressive strength test results also show that both scaffolds have mechanical properties similar to the cancellous bone. Young's modulus and density increase, and porosity and water absorption decrease by increasing the content of the hydroxyapatite composite. Despite the suitability of both methods, it seems that the biomimetic-made scaffolds are more suitable due to the higher density, higher tolerance levels of stress and Young's modulus, lower crystallinity, and replacement of carbonate ions appropriate method.
کلیدواژه ها:
نویسندگان
marzieh khorshidsavar
amirkabir university
mobina khakbaz
university Amirkabir
gity mir mohammad sadeghi
AMIRKABIR UNIVERSITY
mostafa moradi
Amirkabir University